- 密度 [g/cm3]: 1.2
- 弯曲强度 [MPa]: 48.3
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | |
| Moisture Absorption at Equilibrium | 0.50 % | 0.50 % | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 75 | 75 | |
| Tensile Strength, Ultimate | 48.3 MPa | 7000 psi | |
| Elongation at Break | 1.5 % | 1.5 % | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | |
| Dielectric Strength | 15.7 kV/mm | 400 kV/in | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C | 25.0 µin/in-°F @Temperature 68.0 °F | |
| Thermal Conductivity | 1.15 W/m-K | 8.00 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 232 °C | 450 °F | |
| Shrinkage | 0.30 % | 0.30 % | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 30.0 min | 0.500 hour | at 250°F |