- 密度 [g/cm3]: 1.1
- 弯曲强度 [MPa]: 34.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | |
| Moisture Absorption at Equilibrium | 0.80 % | 0.80 % | |
| Viscosity | 5000 cP | 5000 cP | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 75 | 75 | |
| Tensile Strength, Ultimate | 34.5 MPa | 5000 psi | |
| Elongation at Break | 3.0 % | 3.0 % | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 62.0 µm/m-°C @Temperature 20.0 °C | 34.4 µin/in-°F @Temperature 68.0 °F | |
| Thermal Conductivity | 1.01 W/m-K | 7.00 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 204 °C | 400 °F | |
| Shrinkage | 1.0 % | 1.0 % | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 15.0 min | 0.250 hour | at 250°F |