- 密度 [g/cm3]: 1.32
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | |
| Solids Content | >= 99 % | >= 99 % | |
| Viscosity Measurement | 16 - 26 | 16 - 26 | [sec], Flow Rate (0.104" orifice, 0.7 oz, 65psi) |
| Collected Volatile Condensable Material | 0.00 % | 0.00 % | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 70 | 70 | |
| Adhesive Bond Strength | 0.980 MPa | 142 psi | "Wet" Lap Shear Strength (29.4 MPa Hemming Press.) |
| 1.62 MPa | 235 psi | "Wet" Lap Shear Strength (39.2 MPa Hemming Press.) | |
| 2.04 MPa | 296 psi | "Wet" Lap Shear Strength (49.0 MPa Hemming Press.) | |
| 32.3 MPa @Thickness 1.60 mm | 4690 psi @Thickness 0.0630 in | CRS plate | |
| Peel Strength | 4.24 kN/m | 24.2 pli | |
| Thermal Properties | Metric | English | Comments |
| Flash Point | >= 110 °C | >= 230 °F | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 20.0 min | 0.333 hour | 338°F |