- 弯曲强度 [MPa]: 31.0
- 弯曲模量 [MPa]: 2.07
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 300 cP @Temperature 25.0 °C | 300 cP @Temperature 77.0 °F | Hardener | ||
| 500 cP @Temperature 25.0 °C | 500 cP @Temperature 77.0 °F | Mixed | |||
| 600 cP @Temperature 25.0 °C | 600 cP @Temperature 77.0 °F | Resin | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 78 | 78 | |||
| Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | |||
| Elongation at Break | 12 % | 12 % | |||
| Tensile Modulus | 1.45 GPa | 210 ksi | |||
| Flexural Strength | 65.5 MPa | 9500 psi | |||
| Flexural Modulus | 2.07 GPa | 300 ksi | |||
| Compressive Yield Strength | 44.8 MPa | 6500 psi | |||
| Compressive Modulus | 1.59 GPa | 230 ksi | |||
| Thermal Properties | Metric | English | Comments | ||
| Flash Point | 103 °C | 217 °F | Hardener, closed cup | ||
| 177 °C | 351 °F | Resin, closed cup | |||
| Optical Properties | Metric | English | Comments | ||
| Gardner Color Number | 3.0 | 3.0 | Resin | ||
| 5.0 | 5.0 | Mix | |||
| 8.0 | 8.0 | Hardener | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 min | 1.00 hour | Working Time @ 25°C (77°F) | ||
| 720 min | 12.0 hour | Thin Film Set @ 25°C (77°F) | |||
| 1440 min | 24.0 hour | ||||
| 10100 min | 168 hour | Maximum Cure @ 25°C (77°F) | |||
| Descriptive Properties | |||||
| Mar Resistance | 1.05 kg | ||||