- 密度 [g/cm3]: 1.18
- 弯曲模量 [MPa]: 19.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | |||
| Viscosity | 750 cP | 750 cP | ASTM D2293 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 88 | 88 | Cured; ASTM D2240 | ||
| Tensile Strength at Break | 281.8 MPa | 40870 psi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D638 | ||
| Elongation at Break | 1.97 % | 1.97 % | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D638 | ||
| Tensile Modulus | 14.7 GPa | 2130 ksi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content. | ||
| Flexural Strength | 308.98 MPa | 44814 psi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D790 | ||
| Flexural Modulus | 19.5 GPa | 2830 ksi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Glass Transition Temp, Tg | 64.4 °C | 148 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 120 min | 120 min | Value for 4 fl. Oz. at 77°F; ASTM D2471 | ||
| Descriptive Properties | |||||
| Mix Ratio | 100:44 | Resin:Hardener by Weight | |||
| 2.13:1 | Resin:Hardener by Volume | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.