- 密度 [g/cm3]: 1.12
- 弯曲模量 [MPa]: 21.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.12 - 1.13 g/cc | 0.0405 - 0.0408 lb/in³ | |||
| Viscosity | 925 cP | 925 cP | ASTM D2293 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 87 | 87 | Cured; ASTM D2240 | ||
| Tensile Strength at Break | 316.3 MPa | 45870 psi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D638 | ||
| Elongation at Break | 1.98 % | 1.98 % | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D638 | ||
| Tensile Modulus | 17.4 GPa | 2520 ksi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content. | ||
| Flexural Strength | 459.65 MPa | 66667 psi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D790 | ||
| Flexural Modulus | 21.0 GPa | 3050 ksi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 74.7 µm/m-°C @Temperature 37.8 - 65.6 °C | 41.5 µin/in-°F @Temperature 100 - 150 °F | ASTM D696 | ||
| Glass Transition Temp, Tg | 90.0 °C | 194 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 120 min | 120 min | Value for 4 fl. Oz. at 77°F; ASTM D2471 | ||
| Descriptive Properties | |||||
| Color | Amber | ||||
| Mix Ratio | 100:27 | Resin:Hardener by Weight | |||
| 3:1 | Resin:Hardener by Volume | ||||