| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Storage Temperature | 4.00 °C | 39.2 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 40.0 MPa | 5800 psi | |||
| Elongation at Break | 2.5 % | 2.5 % | |||
| Tensile Modulus | 2.25 GPa | 326 ksi | |||
| Compressive Strength | 116.6 MPa | 16910 psi | |||
| Compressive Modulus | 4.00 GPa | 580 ksi | |||
| Adhesive Bond Strength | 10.3 MPa @Temperature 93.0 °C | 1490 psi @Temperature 199 °F | Tensile Lap Shear | ||
| 12.4 MPa @Temperature -55.0 °C | 1800 psi @Temperature -67.0 °F | Tensile Lap Shear | |||
| 15.9 MPa @Temperature 25.0 °C | 2310 psi @Temperature 77.0 °F | Tensile Lap Shear | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 149 °C | 300 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 min @Temperature 93.0 °C | 1.00 hour @Temperature 199 °F | |||
| 7200 - 10100 min @Temperature 25.0 °C | 120 - 168 hour @Temperature 77.0 °F | ||||
| Pot Life | 30 min | 30 min | |||
| Descriptive Properties | |||||
| Consistency | Low Viscosity | ||||
| Form | 2 parts | ||||
| Mix Ratio, Part A:Part B | 100:58 | ||||
| Peel Strength | Nil | ||||