- 密度 [g/cm3]: 1.24
- 拉伸强度 [MPa]: 69.0
- 断裂伸长率 [%]: 117
- 弯曲模量 [MPa]: 3.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 69.0 MPa @Temperature 23.0 °C | 10000 psi @Temperature 73.4 °F | |
| Elongation at Break | 2.59 % | 2.59 % | |
| Tensile Modulus | 3.00 GPa @Temperature 23.0 °C | 435 ksi @Temperature 73.4 °F | |
| Flexural Yield Strength | 117 MPa | 17000 psi | Room Temperature |
| 82.0 MPa @Temperature 163 °C | 11900 psi @Temperature 325 °F | Wet (Immersion at 170°F for 7 days) | |
| 87.0 MPa @Temperature 177 °C | 12600 psi @Temperature 351 °F | ||
| 93.0 MPa @Temperature 163 °C | 13500 psi @Temperature 325 °F | ||
| Flexural Modulus | 3.00 GPa | 435 ksi | Room Temperature |
| 2.30 GPa @Temperature 163 °C | 334 ksi @Temperature 325 °F | Wet (Immersion at 170°F for 7 days) | |
| 2.40 GPa @Temperature 177 °C | 348 ksi @Temperature 351 °F | ||
| 2.40 GPa @Temperature 163 °C | 348 ksi @Temperature 325 °F | ||
| Poissons Ratio | 0.38 | 0.38 | |
| Shear Modulus | 1.09 GPa | 158 ksi | Calculated |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.92 | 2.92 | |
| 2.92 | 2.92 | ||
| 3.13 @Frequency 1.00e+10 Hz | 3.13 @Frequency 1.00e+10 Hz | Moisture Conditioned: 71°C and 95% RH for 140 days; Room Temperature; ASTM D2520 | |
| 3.29 @Frequency 1.00e+10 Hz, Temperature 163 °C | 3.29 @Frequency 1.00e+10 Hz, Temperature 325 °F | Moisture Conditioned: 71°C and 95% RH for 140 days; ASTM D2520 | |
| Dielectric Loss Index | 0.0080 | 0.0080 | Room Temperature |
| 0.010 @Temperature 163 °C | 0.010 @Temperature 325 °F | ||
| 0.010 @Frequency 1.00e+10 Hz | 0.010 @Frequency 1.00e+10 Hz | Moisture Conditioned: 71°C and 95% RH for 140 days; Room Temperature; ASTM D2520 | |
| 0.020 @Frequency 1.00e+10 Hz, Temperature 163 °C | 0.020 @Frequency 1.00e+10 Hz, Temperature 325 °F | Moisture Conditioned: 71°C and 95% RH for 140 days; ASTM D2520 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 50.8 µm/m-°C | 28.2 µin/in-°F | |
| Glass Transition Temp, Tg | 191 °C | 376 °F | |