- 密度 [g/cm3]: 1.26
- 拉伸强度 [MPa]: 59.0
- 断裂伸长率 [%]: 94.0
- 弯曲模量 [MPa]: 2.40
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | Cured resin density |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 59.0 MPa | 8560 psi | ISO R527 |
| Elongation at Yield | 1.7 % | 1.7 % | ISO R527 |
| Tensile Modulus | 3.54 GPa | 513 ksi | ISO R527 |
| Flexural Yield Strength | 94.0 MPa | 13600 psi | ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Glass Transition Temp, Tg | 190 - 210 °C | 374 - 410 °F | DMA |
| Processing Properties | Metric | English | Comments |
| Shelf Life | 12.0 Month @Temperature -18.0 °C | 12.0 Month @Temperature -0.400 °F | |