- 拉伸强度 [MPa]: 2680.0
- 断裂伸长率 [%]: 87.6
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 2680 MPa @Temperature 23.0 °C | 389000 psi @Temperature 73.4 °F | 0° |
| Tensile Modulus | 160 GPa @Temperature 23.0 °C | 23200 ksi @Temperature 73.4 °F | 0° |
| Flexural Yield Strength | 87.6 MPa | 12700 psi | 90°, Room Temperature |
| Compressive Yield Strength | 207 MPa | 30000 psi | Compression After Impact; Room Temperature |
| 285 MPa | 41300 psi | Open Hole Compression; Room Temperature | |
| 1420 MPa | 206000 psi | 0°, Room Temperature | |
| 216 MPa @Temperature 177 °C | 31300 psi @Temperature 351 °F | Open Hole Compression; Wet | |
| 224 MPa @Temperature 163 °C | 32500 psi @Temperature 325 °F | Open Hole Compression; Wet | |
| 236 MPa @Temperature 149 °C | 34200 psi @Temperature 300 °F | Open Hole Compression; Wet | |
| 1000 MPa @Temperature 163 °C | 145000 psi @Temperature 325 °F | 0° | |
| 1030 MPa @Temperature 177 °C | 149000 psi @Temperature 351 °F | 0° | |
| 1410 MPa @Temperature 149 °C | 205000 psi @Temperature 300 °F | 0°, Wet | |
| Shear Modulus | 4.27 GPa | 619 ksi | In-Plane; Room Temperature |
| 2.76 GPa @Temperature 163 °C | 400 ksi @Temperature 325 °F | In-Plane; Wet | |
| 2.90 GPa @Temperature 149 °C | 421 ksi @Temperature 300 °F | In-Plane; Wet | |
| Shear Strength | 100 MPa | 14500 psi | Short Beam; Room Temperature |
| 46.2 MPa @Temperature 163 °C | 6700 psi @Temperature 325 °F | Short Beam, Wet | |
| 48.3 MPa @Temperature 149 °C | 7010 psi @Temperature 300 °F | Short Beam, Wet | |
| 49.6 MPa @Temperature 177 °C | 7190 psi @Temperature 351 °F | Short Beam | |
| 49.6 MPa @Temperature 177 °C | 7190 psi @Temperature 351 °F | Short Beam, Wet | |
| 58.6 MPa @Temperature 163 °C | 8500 psi @Temperature 325 °F | Short Beam | |
| 63.4 MPa @Temperature 149 °C | 9200 psi @Temperature 300 °F | Short Beam | |