- 密度 [g/cm3]: 1.272
- 拉伸强度 [MPa]: 99.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.272 g/cc | 0.04595 lb/in³ | |||
| Moisture Absorption at Equilibrium | 3.1 % | 3.1 % | |||
| Viscosity | 1900 cP @Temperature 129 - 149 °C | 1900 cP @Temperature 264 - 300 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 99.3 MPa | 14400 psi | |||
| Elongation at Yield | 4.4 % | 4.4 % | |||
| Tensile Modulus | 4.09 GPa | 593 ksi | |||
| Fracture Toughness | 3.51 MPa-m½ | 3.19 ksi-in½ | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 93.3 °C | 200 °F | |||
| Glass Transition Temp, Tg | 116 °C | 241 °F | Wet | ||
| 157 °C | 315 °F | Dry | |||
| Processing Properties | Metric | English | Comments | ||
| Gel Time | 8.00 - 16.0 min @Temperature 177 °C | 8.00 - 16.0 min @Temperature 351 °F | |||
| Descriptive Properties | |||||
| Tack Life (days) | 40 | ||||