- 密度 [g/cm3]: 1.7
- 弯曲模量 [MPa]: 12.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0016 cm/cm | 0.0016 in/in | parallel; DIN 53 464 | ||
| Linear Mold Shrinkage, Transverse | 0.0043 cm/cm | 0.0043 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Flexural Strength | 160 - 180 MPa | 23200 - 26100 psi | ISO 178 | ||
| Flexural Modulus | 12.0 - 13.0 GPa | 1740 - 1890 ksi | ISO 178 | ||
| Charpy Impact Unnotched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | DIN 53 483 | ||
| Surface Resistance | >= 1.00e+11 ohm | >= 1.00e+11 ohm | DIN 53 482 | ||
| Dielectric Constant | 6.0 - 7.0 | 6.0 - 7.0 | DIN 53 483 | ||
| Dissipation Factor | 0.080 @Frequency 1000 Hz | 0.080 @Frequency 1000 Hz | tan delta; DIN 53 483 | ||
| Arc Resistance | >= 130 sec | >= 130 sec | ASTM D495 | ||
| Comparative Tracking Index | >= 700 V | >= 700 V | IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 0.258 W/m-K | 1.79 BTU-in/hr-ft²-°F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 270 °C | >= 518 °F | ISO 175 | ||
| Deflection Temperature at 8.0 MPa | 170 °C | 338 °F | ISO 175 | ||
| Flammability, UL94 | V-0 | V-0 | |||
| Oxygen Index | >= 30 % | >= 30 % | ASTM D2863 | ||
| Shrinkage | 0.45 % | 0.45 % | parallel, Post Shrinkage; DIN 53 464 | ||
| 0.85 % | 0.85 % | transverse, Post Shrinkage | |||
| Descriptive Properties | |||||
| Glow Bar 960°C 180 sec | BH2-5 | IEC 707 | |||
| Water Absorption [mg] | <200 | DIN 53 495/23°C 96h | |||