- 密度 [g/cm3]: 0.31
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.310 g/cc | 0.0112 lb/in³ | |
| Density | 0.310 g/cc | 0.0112 lb/in³ | |
| Thickness | 254 microns | 10.0 mil | Nominal |
| 259 microns | 10.2 mil | Typical; TAPPI-411 | |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 3.4 % | 3.4 % | ASTM D828 |
| Film Elongation at Break, TD | 5.2 % | 5.2 % | ASTM D828 |
| Tear Strength, Total | 8.00 N | 1.80 lb (f) | Initial in TD; ASTM D1004 |
| 13.0 N | 2.92 lb (f) | Initial in MD; ASTM D1004 | |
| Elmendorf Tear Strength, MD | 0.748 g/micron | 19.0 g/mil | Calculated from mfr's report of 1.9 N per TAPPI-414 and the typical thickness |
| Elmendorf Tear Strength, TD | 0.984 g/micron | 25.0 g/mil | Calculated from mfr's report of 2.5 N per TAPPI-414 and the typical thickness |
| Film Tensile Strength at Break, MD | 13.5 MPa | 1960 psi | Calculated from mfr's report of 35 N/cm per ASTM D828 and the typical thickness |
| Film Tensile Strength at Break, TD | 7.70 MPa | 1120 psi | Calculated from mfr's report of 20 N/cm per ASTM D828 and the typical thickness |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 1.2 @Frequency 60 Hz | 1.2 @Frequency 60 Hz | ASTM D150 |
| 1.3 @Frequency 1000 Hz | 1.3 @Frequency 1000 Hz | ASTM D150 | |
| Dielectric Strength | 9.00 kV/mm | 229 kV/in | AC Rapid Rise; ASTM D149 |
| 18.0 kV/mm | 457 kV/in | Full-wave Impulse; ASTM D3426 | |
| Dissipation Factor | 0.0030 @Frequency 60 Hz | 0.0030 @Frequency 60 Hz | ASTM D150 |
| 0.0050 @Frequency 1000 Hz | 0.0050 @Frequency 1000 Hz | ASTM D150 | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 220 °C | 428 °F | Electrical insulation |
| Shrinkage, MD | 0.60 % | 0.60 % | at 240°C |
| Shrinkage, TD | 0.90 % | 0.90 % | at 240°C |