- 密度 [g/cm3]: 0.94
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.940 g/cc | 0.0340 lb/in³ | |
| Density | 0.940 g/cc | 0.0340 lb/in³ | |
| Thickness | 178 microns | 7.00 mil | Nominal |
| 188 microns | 7.40 mil | Typical; ASTM D374 | |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 13.1 % | 13.1 % | ASTM D828 |
| Film Elongation at Break, TD | 15.9 % | 15.9 % | ASTM D828 |
| Flex Crack Resistance | 8600 | 8600 | Cycles of Fold Endurance; ASTM D2176 |
| Tear Strength, Total | 24.0 N | 5.40 lb (f) | Initial in TD; ASTM D1004 |
| 55.0 N | 12.4 lb (f) | Initial in MD; ASTM D1004 | |
| Film Tensile Strength at Break, MD | 91.5 MPa | 13300 psi | Calculated from mfr's report of 172 N/cm per ASTM D828 and the typical thickness |
| Film Tensile Strength at Break, TD | 42.0 MPa | 6090 psi | Calculated from mfr's report of 79 N/cm per ASTM D828 and the typical thickness |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | 50% RH; tested on 10 mil thickness sample; ASTM D257 |
| Dielectric Constant | 2.5 @Frequency 60 Hz | 2.5 @Frequency 60 Hz | ASTM D150 |
| 2.5 @Frequency 1000 Hz | 2.5 @Frequency 1000 Hz | ASTM D150 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | AC Rapid Rise; ASTM D149 |
| 51.0 kV/mm | 1300 kV/in | Full-wave Impulse; ASTM D3426 | |
| Dissipation Factor | 0.0080 @Frequency 60 Hz | 0.0080 @Frequency 60 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 220 °C | 428 °F | Electrical insulation |