- 密度 [g/cm3]: 0.0801
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0801 g/cc | 0.00289 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 3.52 MPa | >= 510 psi | Bare, min |
| >= 3.79 MPa | >= 550 psi | Stabilized, min | |
| 4.83 MPa | 700 psi | Bare, typ | |
| 5.14 MPa | 745 psi | Stabilized, typ | |
| Shear Modulus | 0.0448 GPa | 6.50 ksi | Plate Shear, W Direction, typ, preliminary value obtained from limited testing |
| 0.0827 GPa | 12.0 ksi | Plate Shear, L Direction, typ, preliminary value obtained from limited testing | |
| Shear Strength | >= 1.10 MPa | >= 160 psi | Plate Shear, W Direction, min, preliminary value obtained from limited testing |
| 1.41 MPa | 205 psi | Plate Shear, W Direction, typ, preliminary value obtained from limited testing | |
| >= 1.86 MPa | >= 270 psi | Plate Shear, L Direction, min, preliminary value obtained from limited testing | |
| 2.45 MPa | 355 psi | Plate Shear, L Direction, typ, preliminary value obtained from limited testing | |