- 密度 [g/cm3]: 0.032
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0320 g/cc | 0.00116 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 0.793 MPa | >= 115 psi | Bare, min |
| >= 0.862 MPa | >= 125 psi | Stabilized, min | |
| 0.965 MPa | 140 psi | Bare, typ | |
| 1.07 MPa | 155 psi | Stabilized, typ | |
| Compressive Modulus | 0.0758 GPa | 11.0 ksi | Stabilized, typ |
| Shear Modulus | 0.0138 GPa | 2.00 ksi | Plate Shear, W Direction, typ |
| 0.0276 GPa | 4.00 ksi | Plate Shear, L Direction, typ | |
| Shear Strength | >= 0.276 MPa | >= 40.0 psi | Plate Shear, W Direction, min |
| 0.345 MPa | 50.0 psi | Plate Shear, W Direction, typ | |
| >= 0.586 MPa | >= 85.0 psi | Plate Shear, L Direction, min | |
| 0.724 MPa | 105 psi | Plate Shear, L Direction, typ | |