- 密度 [g/cm3]: 1.36
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Density | 1.36 g/cc | 0.0492 lb/in³ | |||
Mechanical Properties | Metric | English | Comments | ||
Tensile Strength | 6.89 MPa | 1000 psi | across grain; ASTM F152 | ||
Electrical Properties | Metric | English | Comments | ||
Dielectric Strength | >= 15.2 kV/mm @Temperature 121 °C, Time 10800 sec | >= 385 kV/in @Temperature 250 °F, Time 3.00 hour | 0.0625 in. thickness; ASTM D149 | ||
<= 0.394 kV/mm @Thickness 1.59 mm | <= 10.0 kV/in @Thickness 0.0625 in | 100% RH for 96 hours; ASTM D149 | |||
<= 0.394 kV/mm @Thickness 3.17 mm | <= 10.0 kV/in @Thickness 0.125 in | 100% RH for 96 hours; ASTM D149 | |||
Thermal Properties | Metric | English | Comments | ||
Maximum Service Temperature, Air | 204 °C @Pressure 3.45 MPa | 400 °F @Pressure 500 psi | Continuous | ||
Minimum Service Temperature, Air | -73.3 °C | -100 °F | |||
Descriptive Properties | |||||
Color | Blue/Off-White | ||||
Compressibility, % | 15-30 | ASTM F36 | |||
Creep Relaxation, % | 30 | ASTM F38 | |||
Sealability ASTM F37B, ml/hr | 0.15 | ASTM Fuel A | |||
0.2 | Nitrogen |