| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Moisture Absorption at Equilibrium | 5.7 % @Thickness 1.57 mm | 5.7 % @Thickness 0.0620 in | ASTM D229 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Modulus of Elasticity | 8.27 GPa @Thickness 1.57 mm | 1200 ksi @Thickness 0.0620 in | LW; ASTM D229 | ||
| 8.27 GPa @Thickness 1.57 mm | 1200 ksi @Thickness 0.0620 in | CW; ASTM D229 | |||
| Flexural Strength | 89.6 MPa @Thickness 1.57 mm | 13000 psi @Thickness 0.0620 in | CW; ASTM D790 | ||
| 234 MPa @Thickness 1.57 mm | 34000 psi @Thickness 0.0620 in | LW; ASTM D790 | |||
| Compressive Strength | 290 MPa @Thickness 12.7 mm | 42000 psi @Thickness 0.500 in | ASTM D695 | ||
| Izod Impact, Unnotched | 4.81 J/cm @Thickness 12.7 mm | 9.00 ft-lb/in @Thickness 0.500 in | CW, Cond E-48/50; ASTM D256 | ||
| 17.1 J/cm @Thickness 12.7 mm | 32.0 ft-lb/in @Thickness 0.500 in | LW, Cond E-48/50; ASTM D256 | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 8.0 @Thickness 1.57 mm | 8.0 @Thickness 0.0620 in | Permittivity, Cond D-24/23; ASTM D150 | ||
| Dielectric Breakdown | 11000 V @Thickness 1.57 mm | 11000 V @Thickness 0.0620 in | Cond D-48/50; ASTM D229 S/S | ||
| 53000 V @Thickness 1.57 mm | 53000 V @Thickness 0.0620 in | Cond A; ASTM D229 S/S | |||
| Dissipation Factor | 0.040 @Thickness 1.57 mm | 0.040 @Thickness 0.0620 in | Cond D-24/23; ASTM D150 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 18.0 µm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C | 10.0 µin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F | x-axis; IPC-TM 650-2.4.24 | ||
| CTE, linear, Transverse to Flow | 11.0 µm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C | 6.11 µin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F | x-axis; IPC-TM 650-2.4.24 | ||
| Descriptive Properties | |||||
| Bond Strength | 2000 lb | 0.5", ASTM D229 | |||
| Color | Natural | ||||