- 密度 [g/cm3]: 1.03
- 吸水率 [%]: 0.05
- 缺口冲击强度: 2.14
- 断裂伸长率 [%]: 40.0
- 弯曲强度 [MPa]: 30.3
- 弯曲模量 [MPa]: 3.45
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 - 1.95 g/cc | 0.0372 - 0.0704 lb/in³ | Average value: 1.72 g/cc Grade Count:31 |
| Water Absorption | 0.0500 - 0.600 % | 0.0500 - 0.600 % | Average value: 0.257 % Grade Count:22 |
| Linear Mold Shrinkage | 0.000 - 0.00100 cm/cm | 0.000 - 0.00100 in/in | Average value: 0.000449 cm/cm Grade Count:12 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 35.0 - 70.0 | 35.0 - 70.0 | Average value: 53.8 Grade Count:15 |
| Tensile Strength, Ultimate | 30.3 - 993 MPa | 4400 - 144000 psi | Average value: 206 MPa Grade Count:30 |
| 58.6054 - 58.6054 MPa @Temperature 150 - 150 °C | 8500.01 - 8500.01 psi @Temperature 302 - 302 °F | Average value: 58.6 MPa Grade Count:1 | |
| Elongation at Break | 1.20 - 7.90 % | 1.20 - 7.90 % | Average value: 3.47 % Grade Count:3 |
| Modulus of Elasticity | 3.72 - 94.5 GPa | 540 - 13700 ksi | Average value: 19.7 GPa Grade Count:16 |
| 8.27371 - 8.27371 GPa @Temperature 150 - 150 °C | 1200.02 - 1200.02 ksi @Temperature 302 - 302 °F | Average value: 8.27 GPa Grade Count:1 | |
| Flexural Yield Strength | 40.0 - 1310 MPa | 5800 - 190000 psi | Average value: 301 MPa Grade Count:31 |
| 120.658 - 365 MPa @Temperature 115 - 150 °C | 17500.0 - 52900 psi @Temperature 239 - 302 °F | Average value: 243 MPa Grade Count:2 | |
| Flexural Modulus | 3.45 - 77.9 GPa | 500 - 11300 ksi | Average value: 16.1 GPa Grade Count:26 |
| 16.2 - 16.2 GPa @Temperature 115 - 115 °C | 2350 - 2350 ksi @Temperature 239 - 239 °F | Average value: 9.03 GPa Grade Count:1 | |
| 6.20528 - 8.27371 GPa @Temperature 150 - 150 °C | 900.014 - 1200.02 ksi @Temperature 302 - 302 °F | Average value: 9.03 GPa Grade Count:1 | |
| 6.20528 - 8.27371 GPa @Thickness 0.500 - 2.50 mm | 900.014 - 1200.02 ksi @Thickness 0.0197 - 0.0984 in | Average value: 9.03 GPa Grade Count:1 | |
| Compressive Yield Strength | 103 - 310 MPa | 15000 - 45000 psi | Average value: 198 MPa Grade Count:16 |
| Compressive Modulus | 0.0172 - 33.8 GPa | 2.49 - 4900 ksi | Average value: 12.2 GPa Grade Count:7 |
| Ultimate Bearing Strength | 221 MPa | 32000 psi | Average value: 221 MPa Grade Count:3 |
| Poissons Ratio | 0.305 - 0.330 | 0.305 - 0.330 | Average value: 0.324 Grade Count:4 |
| Shear Modulus | 3.10 - 5.19 GPa | 450 - 753 ksi | Average value: 4.40 GPa Grade Count:3 |
| Shear Strength | 31.0 - 96.5 MPa | 4500 - 14000 psi | Average value: 49.4 MPa Grade Count:5 |
| Izod Impact, Notched | 2.14 - 37.0 J/cm | 4.00 - 69.3 ft-lb/in | Average value: 10.9 J/cm Grade Count:23 |
| Izod Impact, Unnotched | 0.160 - 19.2 J/cm | 0.300 - 36.0 ft-lb/in | Average value: 12.3 J/cm Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.0100 - 5.00e+14 ohm-cm | 0.0100 - 5.00e+14 ohm-cm | Average value: 2.00e+14 ohm-cm Grade Count:4 |
| Dielectric Constant | 4.70 - 5.00 | 4.70 - 5.00 | Average value: 4.80 Grade Count:3 |
| Dielectric Strength | 1.38 - 20.0 kV/mm | 35.0 - 508 kV/in | Average value: 10.2 kV/mm Grade Count:13 |
| Arc Resistance | 120 - 191 sec | 120 - 191 sec | Average value: 147 sec Grade Count:12 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 8.00 - 36.0 µm/m-°C | 4.44 - 20.0 µin/in-°F | Average value: 20.8 µm/m-°C Grade Count:11 |
| CTE, linear, Transverse to Flow | 18.0 - 27.0 µm/m-°C | 10.0 - 15.0 µin/in-°F | Average value: 23.0 µm/m-°C Grade Count:4 |
| Specific Heat Capacity | 0.841 - 1.51 J/g-°C | 0.201 - 0.360 BTU/lb-°F | Average value: 1.28 J/g-°C Grade Count:3 |
| Thermal Conductivity | 0.300 - 46.2 W/m-K | 2.08 - 321 BTU-in/hr-ft²-°F | Average value: 11.1 W/m-K Grade Count:5 |
| 18.5 - 43.7 W/m-K @Temperature 85.0 - 85.0 °C | 128 - 303 BTU-in/hr-ft²-°F @Temperature 185 - 185 °F | Average value: 31.1 W/m-K Grade Count:1 | |
| Maximum Service Temperature, Air | 98.0 - 300 °C | 208 - 572 °F | Average value: 227 °C Grade Count:6 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 - 271 °C | 320 - 520 °F | Average value: 237 °C Grade Count:7 |
| Glass Transition Temp, Tg | 118 - 200 °C | 244 - 392 °F | Average value: 169 °C Grade Count:7 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:10 |
| Flame Spread Index | 25.0 | 25.0 | Average value: 25.0 Grade Count:4 |
| NBS Smoke Density | 600 - 700 | 600 - 700 | Average value: 650 Grade Count:3 |
| Shrinkage | 0.000 - 0.00100 % | 0.000 - 0.00100 % | Average value: 0.000600 % Grade Count:7 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 93.0 - 160 °C | 199 - 320 °F | Average value: 139 °C Grade Count:11 |
| Cure Time | 5.00 - 10.0 min @Temperature 138 - 138 °C | 0.0833 - 0.167 hour @Temperature 280 - 280 °F | Average value: 5.17 min Grade Count:1 |
| 3.00 - 5.00 min @Temperature 138 - 138 °C | 0.0500 - 0.0833 hour @Temperature 280 - 280 °F | Average value: 5.17 min Grade Count:1 | |
| 3.00 - 5.00 min @Thickness 6.35 - 6.35 mm | 0.0500 - 0.0833 hour @Thickness 0.250 - 0.250 in | Average value: 5.17 min Grade Count:1 | |
| Shelf Life | 2.00 - 3.00 Month | 2.00 - 3.00 Month | Average value: 2.25 Month Grade Count:4 |