- 密度 [g/cm3]: 2.1
- 弯曲模量 [MPa]: 6.23
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.10 g/cc | 0.0759 lb/in³ | Cured |
| Volatile Organic Compounds (VOC) Content | 550 g/l @Temperature 43.0 °C | 550 g/l @Temperature 109 °F | EPA 24 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 89 | 89 | ASTM D2240 |
| Elongation at Break | 1.04 % | 1.04 % | ASTM D638 |
| Flexural Strength | 51.7 MPa | 7500 psi | ASTM D790 |
| Flexural Modulus | 6.23 GPa | 903 ksi | ASTM D790 |
| Compressive Strength | 110 MPa | 16000 psi | ASTM D695 |
| Adhesive Bond Strength | >= 16.3 MPa | >= 2370 psi | ASTM D4541 |
| Impact Test | 9.04 J | 6.67 ft-lb | direct; ASTM D2794 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 135 °C | 275 °F | Wet Service (water) |
| 180 °C | 356 °F | Dry Service (continuous) | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 60.0 min @Temperature 29.0 °C | 1.00 hour @Temperature 84.2 °F | Overcoat Begin |
| 70.02 min @Temperature 29.0 °C | 1.167 hour @Temperature 84.2 °F | Tack Free without MEK | |
| 76.02 min @Temperature 29.0 °C | 1.267 hour @Temperature 84.2 °F | Tack Free with MEK | |
| 100 min @Temperature 21.0 °C | 1.67 hour @Temperature 69.8 °F | Tack Free without MEK | |
| 120 min @Temperature 16.0 °C | 2.00 hour @Temperature 60.8 °F | Tack Free without MEK | |
| 120 min @Temperature 21.0 °C | 2.00 hour @Temperature 69.8 °F | Tack Free with MEK | |
| 120 min @Temperature 21.0 °C | 2.00 hour @Temperature 69.8 °F | Overcoat Begin | |
| 140 min @Temperature 10.0 °C | 2.33 hour @Temperature 50.0 °F | Tack Free without MEK | |
| 180 min @Temperature 10.0 °C | 3.00 hour @Temperature 50.0 °F | Tack Free with MEK | |
| 180 min @Temperature 29.0 °C | 3.00 hour @Temperature 84.2 °F | Overcoat End | |
| 240 min @Temperature 21.0 °C | 4.00 hour @Temperature 69.8 °F | Overcoat End | |
| 270 min @Temperature 16.0 °C | 4.50 hour @Temperature 60.8 °F | Overcoat End | |
| 300 min @Temperature 10.0 °C | 5.00 hour @Temperature 50.0 °F | Overcoat End | |
| 360 min @Temperature 16.0 °C | 6.00 hour @Temperature 60.8 °F | Overcoat Begin | |
| 720 min @Temperature 10.0 °C | 12.0 hour @Temperature 50.0 °F | Overcoat Begin | |
| 960 min @Temperature 29.0 °C | 16.0 hour @Temperature 84.2 °F | Full Chemical | |
| 1440 min @Temperature 21.0 °C | 24.0 hour @Temperature 69.8 °F | Full Chemical | |
| 1500 min @Temperature 16.0 °C | 25.0 hour @Temperature 60.8 °F | Tack Free with MEK | |
| 2880 min @Temperature 16.0 °C | 48.0 hour @Temperature 60.8 °F | Full Chemical | |
| 4320 min @Temperature 10.0 °C | 72.0 hour @Temperature 50.0 °F | Full Chemical | |