- 密度 [g/cm3]: 1.55
- 断裂伸长率 [%]: 450
- 弯曲强度 [MPa]: 300.0
- 弯曲模量 [MPa]: 40.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 300 MPa | 43500 psi | ASTM D638 |
| Tensile Modulus | 45.0 GPa | 6530 ksi | ASTM D638 |
| Flexural Yield Strength | 450 MPa | 65300 psi | ASTM D790 |
| Flexural Modulus | 40.0 GPa | 5800 ksi | ASTM D790 |
| Compressive Yield Strength | 400 MPa | 58000 psi | ASTM D495 |
| Compressive Modulus | 35.0 GPa | 5080 ksi | ASTM D695 |
| Shear Strength | 45.0 MPa | 6530 psi | I.L.S.S. short beam shear per ASTM D5379 |
| Thermal Properties | Metric | English | Comments |
| Glass Transition Temp, Tg | 88.0 °C | 190 °F | by DMTA following AITM 1-0003. Higher Tg possible by adjustment of cure time. |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 135 °C | 275 °F | Cure Temp |