- 缺口冲击强度: 5.3
- 弯曲模量 [MPa]: 10.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.76 g/cc | 1.76 g/cc | |||
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | Polymerization Shrinkage | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 45.0 MPa | 6530 psi | ASTM D638 | ||
| Tensile Modulus | 10.0 GPa | 1450 ksi | ASTM D638 | ||
| Flexural Strength | 128 MPa | 18600 psi | ASTM D790 | ||
| Flexural Modulus | 10.0 GPa | 1450 ksi | ASTM D790 | ||
| Poissons Ratio | 0.30 | 0.30 | |||
| Shear Modulus | 3.80 GPa | 551 ksi | Calculated | ||
| Izod Impact, Notched | 5.30 J/cm | 9.93 ft-lb/in | ASTM D256 | ||
| Izod Impact, Unnotched | 7.00 J/cm | 13.1 ft-lb/in | ASTM D4812 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C | 19.4 µin/in-°F | Z Direction | ||
| CTE, linear, Transverse to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | XY Direction | ||
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 150 °C | 302 °F | Compression Molding | ||
| Clamp Pressure | 3.45 - 6.89 MPa | 500 - 1000 psi | Molding Pressure | ||
| Descriptive Properties | |||||
| Flame Resistance | pass at 3 mm | ANSI Z124.2 | |||
| Stain Resistance | pass | ANSI Z124.2 | |||