- 吸水率 [%]: 0.2
- 弯曲模量 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.74 g/cc | 1.74 g/cc | |
| Water Absorption | 0.20 % | 0.20 % | ISO 62 |
| Linear Mold Shrinkage | 0.00065 cm/cm | 0.00065 in/in | Polymerization Shrinkage |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 40.0 MPa | 5800 psi | ISO 527 |
| Tensile Modulus | 12.0 GPa | 1740 ksi | ISO 527 |
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | Tangent; ISO 178 |
| Poissons Ratio | 0.27 | 0.27 | |
| Shear Modulus | 4.70 GPa | 682 ksi | Calculated |
| Izod Impact, Unnotched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C | 19.4 µin/in-°F | Z Direction |
| CTE, linear, Transverse to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | XY Direction |
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 270 °C | >= 518 °F | ISO 75 |
| Glass Transition Temp, Tg | 204 °C | 399 °F | ASTM D4065-01 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 160 °C | 320 °F | Injection or Injection-Compression Molding |
| Clamp Pressure | <= 6.89 MPa | <= 1000 psi | Molding Pressure |