- 密度 [g/cm3]: 0.104
- 吸水率 [%]: 0.2
- 拉伸强度 [MPa]: 0.0827
- 弯曲强度 [MPa]: 0.0552
- 脆化温度 [℃]: -55.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.104 - 1.64 g/cc | 0.00376 - 0.0592 lb/in³ | Average value: 0.328 g/cc Grade Count:33 |
| Water Absorption | 0.200 - 12.0 % | 0.200 - 12.0 % | Average value: 3.64 % Grade Count:10 |
| Viscosity | 3000 - 55000 cP | 3000 - 55000 cP | Average value: 18000 cP Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 3.00 - 62.0 | 3.00 - 62.0 | Average value: 17.8 Grade Count:7 |
| Hardness, Shore OO | 40.0 - 70.0 | 40.0 - 70.0 | Average value: 53.1 Grade Count:4 |
| Tensile Strength, Ultimate | 0.0552 - 2.80 MPa | 8.00 - 406 psi | Average value: 0.387 MPa Grade Count:15 |
| Tensile Strength, Yield | 0.0827 - 0.689 MPa | 12.0 - 100 psi | Average value: 0.229 MPa Grade Count:6 |
| Elongation at Break | 49.0 - 300 % | 49.0 - 300 % | Average value: 107 % Grade Count:22 |
| Compressive Yield Strength | 0.00800 - 0.170 MPa | 1.16 - 24.7 psi | Average value: 0.0627 MPa Grade Count:19 |
| Compression Set | 0.000 - 15.0 % | 0.000 - 15.0 % | Average value: 3.14 % Grade Count:7 |
| 0.000 - 10.0 % @Temperature 70.0 - 100 °C | 0.000 - 10.0 % @Temperature 158 - 212 °F | Average value: 18.8 % Grade Count:12 | |
| 0.000 - 80.0 % @Time 79200 - 79200 sec | 0.000 - 80.0 % @Time 22.0 - 22.0 hour | Average value: 18.8 % Grade Count:11 | |
| 0.000 - 80.0 % @Temperature 70.0 - 100 °C | 0.000 - 80.0 % @Temperature 158 - 212 °F | Average value: 18.8 % Grade Count:11 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.000100 - 1.00e+14 ohm-cm | 0.000100 - 1.00e+14 ohm-cm | Average value: 7.14e+13 ohm-cm Grade Count:7 |
| Dielectric Constant | 1.30 - 1.58 | 1.30 - 1.58 | Average value: 1.39 Grade Count:6 |
| Dielectric Strength | 3.50 - 7.48 kV/mm | 88.9 - 190 kV/in | Average value: 4.71 kV/mm Grade Count:7 |
| Arc Resistance | 90.0 - 123 sec | 90.0 - 123 sec | Average value: 98.3 sec Grade Count:6 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.0600 - 0.120 W/m-K | 0.416 - 0.833 BTU-in/hr-ft²-°F | Average value: 0.0851 W/m-K Grade Count:6 |
| Maximum Service Temperature, Air | 150 - 280 °C | 302 - 536 °F | Average value: 219 °C Grade Count:17 |
| Minimum Service Temperature, Air | -70.0 - -20.0 °C | -94.0 - -4.00 °F | Average value: -55.4 °C Grade Count:17 |
| Brittleness Temperature | -55.0 °C | -67.0 °F | Average value: -55.0 °C Grade Count:5 |
| Flammability, UL94 | V-1 - V-0 | V-1 - V-0 | Grade Count:14 |
| Flammability Test | 25.0 | 25.0 | Average value: 25.0 Grade Count:5 |
| Flame Spread Index | 11.5 - 25.0 | 11.5 - 25.0 | Average value: 22.6 Grade Count:10 |
| Smoke Density | 1.50 - 50.0 min | 1.50 - 50.0 min | Average value: 15.3 min Grade Count:15 |
| Oxygen Index | 34.0 - 44.0 % | 34.0 - 44.0 % | Average value: 38.7 % Grade Count:6 |
| Shrinkage | <= 5.00 % @Time 605000 - 605000 sec | <= 5.00 % @Time 168 - 168 hour | Average value: 5.00 % Grade Count:2 |
| <= 5.00 % @Temperature 70.0 - 70.0 °C | <= 5.00 % @Temperature 158 - 158 °F | Average value: 5.00 % Grade Count:2 | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 10.0 - 60.0 min | 0.167 - 1.00 hour | Average value: 21.3 min Grade Count:6 |
| 45.0 - 45.0 min @Temperature 100 - 100 °C | 0.750 - 0.750 hour @Temperature 212 - 212 °F | Average value: 45.0 min Grade Count:1 | |