- 密度 [g/cm3]: 1.92
- 吸水率 [%]: 0.24
- 缺口冲击强度: 3.93
- 弯曲模量 [MPa]: 14.7
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.92 g/cc | 0.0694 lb/in³ | ASTM D792 | ||
| Water Absorption | 0.24 % @Temperature 50.0 °C, Time 173000 sec | 0.24 % @Temperature 122 °F, Time 48.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage | 0.0015 - 0.0025 cm/cm | 0.0015 - 0.0025 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 31.0 MPa | 4500 psi | ASTM D638 | ||
| Flexural Strength | 69.0 MPa | 10000 psi | at rupture; ASTM D790 | ||
| Flexural Modulus | 14.7 GPa | 2130 ksi | ASTM D790 | ||
| Compressive Strength | 61.0 MPa | 8850 psi | ASTM D695 | ||
| Izod Impact, Notched | 3.93 J/cm | 7.36 ft-lb/in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz | 4.0 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Dielectric Strength | 3.40 kV/mm @Frequency 60.0 Hz | 86.4 kV/in @Frequency 60.0 Hz | step-by-step, wet; ASTM D149 | ||
| 4.90 kV/mm @Frequency 60.0 Hz | 124 kV/in @Frequency 60.0 Hz | short time, wet; ASTM D149 | |||
| Dissipation Factor | 0.022 @Frequency 1.00e+6 Hz | 0.022 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Arc Resistance | 189 sec | 189 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 282 °C | >= 540 °F | Post Baked; ASTM D648A | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Form | Coarse Flake | ||||
| Molding Method | Compression | ||||
| Transfer | |||||