- 拉伸强度 [MPa]: 5.52
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Specific Gravity | 1.02 g/cc | 1.02 g/cc | "B" component | ||
1.02 g/cc | 1.02 g/cc | "A" component | |||
Viscosity | 18000 cP | 18000 cP | "B" component | ||
31000 cP | 31000 cP | "A" component | |||
Storage Temperature | <= 38.0 °C | <= 100 °F | 12 months | ||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Shore A | 44 | 44 | cured 60 mins @ 150°C | ||
Tensile Strength, Yield | 5.52 MPa | 801 psi | cured 60 mins @ 150°C | ||
Elongation at Break | 200 % | 200 % | cured 60 mins @ 150°C | ||
100% Modulus | 0.00324 GPa | 0.470 ksi | Young's, cured 60 mins @ 150°C | ||
Processing Properties | Metric | English | Comments | ||
Gel Time | >= 4320 min | >= 4320 min | |||
Descriptive Properties | |||||
Color | Blue | "B" component | |||
Translucent | "A" component |