| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | |||
| Solids Content | 38.5 % | 38.5 % | by volume | ||
| 44.8 % | 44.8 % | by weight | |||
| Volatile Organic Compounds (VOC) Content | 119 g/l | 119 g/l | |||
| Viscosity | 300 - 600 cP | 300 - 600 cP | |||
| Thickness | 25.4 microns | 1.00 mil | recommended dry film thickness | ||
| 66.0 microns | 2.60 mil | estimated wet film thickness | |||
| Storage Temperature | 12.8 - 29.4 °C | 55.0 - 85.0 °F | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 593 °C | 1100 °F | |||
| Flash Point | >= 100 °C | >= 212 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 10.0 - 48.9 °C | 50.0 - 120 °F | Application Temperature | ||
| Dry Time | 1.00 - 2.00 hour | 1.00 - 2.00 hour | Touch | ||
| 2.00 - 4.00 hour | 2.00 - 4.00 hour | Handling | |||
| 1.0 - 24.0 hour | 1.0 - 24.0 hour | Recoat | |||
| Cure Time | >= 60.0 min | >= 1.00 hour | Air Set prior to curing | ||
| 60.0 min | 1.00 hour | at 450°F; Adequate ventilation is required when curing these products. Outgassing will occur above 300°F and cease after 750°F. An additional 30 minutes is required at the highest service temperature if service temperature is below 750°F. | |||
| Shelf Life | 12.0 Month | 12.0 Month | |||
| Descriptive Properties | |||||
| Dry Film Coverage ft2/gal | 617 | at 1 mil | |||
| Thinner | Water | ||||