| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | silicone property; Arlon SQA-TMS-024 | ||
| Thickness | 76.2 microns | 3.00 mil | side 1 silicone; Arlon SQA-TMS-003 | ||
| 203 microns | 8.00 mil | substrate; Arlon SQA-TMS-003 | |||
| 229 microns | 9.00 mil | side 2 silicone; Arlon SQA-TMS-003 | |||
| 508 microns | 20.0 mil | overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 60 | 60 | silicone property; ASTM D2240 | ||
| Tensile Strength, Ultimate | 5.52 MPa | 800 psi | silicone property; ASTM D412 | ||
| Elongation at Break | 225 % | 225 % | silicone property; ASTM D412 | ||
| Adhesive Bond Strength | 0.0558 MPa | 8.10 psi | Arlon SQA-TMS-011 | ||
| Tear Strength | 15.8 kN/m | 90.0 pli | silicone property; ASTM D624 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 23.6 kV/mm | 600 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 121 °C | 0.250 hour @Pressure 50.0 psi, Temperature 250 °F | |||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | |||
| Descriptive Properties | |||||
| Color | Red | ||||