- 弯曲强度 [MPa]: 5.69
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | silicone property; Arlon SQA-TMS-024 | ||
| Thickness | 102 microns | 4.00 mil | side 1; Arlon SQA-TMS-003 | ||
| 165 microns | 6.50 mil | side 2; Arlon SQA-TMS-003 | |||
| 483 microns | 19.0 mil | substrate; Arlon SQA-TMS-003 | |||
| 749 microns | 29.5 mil | overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 45 | 45 | silicone property; ASTM D2240 | ||
| Tensile Strength, Ultimate | 5.69 MPa | 825 psi | silicone property; ASTM D412 | ||
| Elongation at Break | 725 % | 725 % | silicone property; ASTM D412 | ||
| Adhesive Bond Strength | 0.0765 MPa | 11.1 psi | Arlon SQA-TMS-011 | ||
| Tear Strength | 28.6 kN/m | 163 pli | Die B; silicone property; ASTM D624 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 23.0 kV/mm | 585 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | |||
| 15.0 min @Pressure 0.345 MPa, Temperature 121 °C | 0.250 hour @Pressure 50.0 psi, Temperature 250 °F | ||||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | |||
| Descriptive Properties | |||||
| Color | Red | ||||
| Flame and Glow Resistance (seconds) | 14400 | FAR 25.853 App. F Pt. 1 Sec. A1ii | |||