- 弯曲强度 [MPa]: 6.07
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | silicone property; Arlon SQA-TMS-024 | ||
| Thickness | 19.0 microns | 0.750 mil | side 1/cured; Arlon SQA-TMS-003 | ||
| 19.0 microns | 0.750 mil | side 2; Arlon SQA-TMS-003 | |||
| 203 microns | 8.00 mil | fiberglass; Arlon SQA-TMS-003 | |||
| 267 microns | 10.5 mil | side1/uncured; Arlon SQA-TMS-003 | |||
| 508 microns | 20.0 mil | overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 50 | 50 | silicone property; ASTM D2240 | ||
| Tensile Strength, Ultimate | 6.07 MPa | 880 psi | silicone property; ASTM D412 | ||
| Elongation at Break | 470 % | 470 % | silicone property; ASTM D412 | ||
| Adhesive Bond Strength | 0.0683 MPa | 9.90 psi | ASTM D624 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 26.4 kV/mm | 670 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 - 180 min @Temperature 204 °C | 2.00 - 3.00 hour @Temperature 400 °F | |||
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | ||||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | |||
| Descriptive Properties | |||||
| Color | Red | ||||