Arlon I51576R015 Silicone Rubber/Fiberglass/Alloy Laminate

Arlon I51576R015 Silicone Rubber/Fiberglass/Alloy Laminate 物性表: Arlon I51576R015 Silicone Rubber/Fiberglass/Alloy Laminate物性表及特性介绍,Arlon I51576R015 Silicone Rubber/Fiberglass/Alloy Laminate注塑参数详情,如需Arlon I51576R015 Silicone Rubber/Fiberglass/Alloy Laminate下载, 可到相关下载区下载
  • 弯曲强度 [MPa]: 6.21
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.15 g/cc1.15 g/ccsilicone property (alloy 600 = 8.41 g/cc); Arlon SQA-TMS-024
Thickness 25.4 microns1.00 millaminated foil; Arlon SQA-TMS-003
 50.8 microns2.00 milside 1; Arlon SQA-TMS-003
 140 microns5.50 milside 2; Arlon SQA-TMS-003
 203 microns8.00 milsubstrate; Arlon SQA-TMS-003
 419 microns16.5 miloverall; Arlon SQA-TMS-003
 
Mechanical PropertiesMetricEnglishComments
Hardness, Shore A 4545silicone property; ASTM D2240
Tensile Strength, Ultimate 6.21 MPa900 psisilicone property; ASTM D412
Elongation at Break 400 %400 %silicone property; ASTM D412
Adhesive Bond Strength 0.0483 MPa7.00 psibond to alloy 600; ASTM D624
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 0.000103 ohm-cm0.000103 ohm-cmalloy 600 property
Dielectric Strength 15.7 kV/mm400 kV/inASTM D149
 
Thermal PropertiesMetricEnglishComments
CTE, linear 13.9 µm/m-°C
@Temperature 20.0 °C
7.72 µin/in-°F
@Temperature 68.0 °F
alloy 600 property
Maximum Service Temperature, Air 232 °C450 °F
Minimum Service Temperature, Air -56.7 °C-70.0 °F
Flammability, UL94 HBHB
 
Processing PropertiesMetricEnglishComments
Cure Time 120 min
@Temperature 204 °C
2.00 hour
@Temperature 400 °F
Shelf Life 12.0 Month
@Temperature 21.1 °C
12.0 Month
@Temperature 70.0 °F

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-33789.html

免责声明: 本文 Arlon I51576R015 Silicone Rubber/Fiberglass/Alloy Laminate 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4