- 密度 [g/cm3]: 1.34
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | Side 2; Arlon SQA-TMS-024 | ||
| 1.56 g/cc | 0.0564 lb/in³ | Side 1; Arlon SQA-TMS-024 | |||
| Thickness | 76.2 microns | 3.00 mil | Interleave | ||
| 102 microns | 4.00 mil | Side 1; Arlon SQA-TMS-003 | |||
| 178 microns | 7.00 mil | Side 2; Arlon SQA-TMS-003 | |||
| 356 microns | 14.0 mil | Substrate; Arlon SQA-TMS-003 | |||
| 635 microns | 25.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 37 | 37 | Side 2; ASTM D2240 | ||
| 55 | 55 | Side 1; ASTM D2240 | |||
| Tensile Strength | 3.65 MPa | 530 psi | Side 1; ASTM D412 | ||
| 6.55 MPa | 950 psi | Side 2; ASTM D412 | |||
| Elongation at Break | 300 % | 300 % | Side 1; ASTM D412 | ||
| 620 % | 620 % | Side 2; ASTM D412 | |||
| Tear Strength | 7.01 kN/m | 40.0 pli | Side 1; ASTM D624 | ||
| 26.3 kN/m | 150 pli | Side 2; ASTM D624 | |||
| Peel Strength | 2.98 kN/m | 17.0 pli | Bond Strength; ASTM D624 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 13.8 kV/mm | 350 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability, UL94 | HB @Temperature 200 °C | HB @Temperature 392 °F | per card E54153 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 28.8 | Arlon SQA-TMS-025 | |||