- 密度 [g/cm3]: 1.18
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 76.2 microns | 3.00 mil | Interleave | ||
| 127 microns | 5.00 mil | Carrier; Arlon SQA-TMS-003 | |||
| 1570 microns | 62.0 mil | Overall; Arlon SQA-TMS-003 | |||
| 1570 microns | 62.0 mil | Side 1; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 50 | 50 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 7.58 MPa | 1100 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 400 % | 400 % | Silicone Property; ASTM D412 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 11.8 kV/mm | 300 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Temperature 177 °C | 0.250 hour @Temperature 350 °F | Recommended Cure Cycle | ||
| 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 54.8 | Arlon SQA-TMS-025 | |||