- 密度 [g/cm3]: 1.2
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 76.2 microns | 3.00 mil | Interleave PE Liner | ||
| 127 microns | 5.00 mil | Interleave PET Carrier | |||
| 1520 microns | 60.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 55 | 55 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 8.96 MPa | 1300 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 700 % | 700 % | Silicone Property; ASTM D412 | ||
| Tear Strength | 35.1 kN/m | 200 pli | Silicone Property; ASTM D624 | ||
| Compression Set | 28 % | 28 % | Silicone Property; ASTM D395 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 30.0 min @Temperature 177 °C | 0.500 hour @Temperature 350 °F | Recommended Cure Cycle | ||
| 240 min @Temperature 227 °C | 4.00 hour @Temperature 440 °F | Recommended Postcure Cycle, after 30 minute ramp up cycle | |||
| Shelf Life | 3.00 Month @Temperature 4.44 °C | 3.00 Month @Temperature 40.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Total Product Weight (oz/yd2) | 52 | Arlon SQA-TMS-025 | |||