- 密度 [g/cm3]: 1.22
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 63.5 microns | 2.50 mil | Interleave | ||
| 127 microns | 5.00 mil | Substrate; Arlon SQA-TMS-003 | |||
| 508 microns | 20.0 mil | Side 1; Arlon SQA-TMS-003 | |||
| 635 microns | 25.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 45 | 45 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 6.38 MPa | 925 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | >= 550 % | >= 550 % | Silicone Property; ASTM D412 | ||
| Peel Strength | 3.86 kN/m | 22.0 pli | Bond Strength; Arlon SQA-TMS-011 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 29.5 kV/mm | 750 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 149 °C | 0.250 hour @Pressure 50.0 psi, Temperature 300 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Gray | ||||
| White | Substrate | ||||
| Total Product Weight (oz/yd2) | 23.8 | Arlon SQA-TMS-025 | |||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.