| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Thickness | 50.8 microns | 2.00 mil | Side 1 | ||
| 76.2 microns | 3.00 mil | Polyethylene Interleave | |||
| 140 microns | 5.50 mil | Prime Coated 1165 Fiberglass, Substrate | |||
| >= 140 microns | >= 5.50 mil | Side 2 | |||
| 305 - 356 microns | 12.0 - 14.0 mil | Overall | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 40 - 50 | 40 - 50 | Compound Property | ||
| Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property | ||
| Elongation at Break | >= 350 % | >= 350 % | Compound Property | ||
| Peel Strength | >= 0.877 kN/m | >= 5.00 pli | Bond Strength | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | White | ||||
| Total Product Weight (oz/yd2) | 12.3 - 15.3 | ||||
| Uncoated Fabric Break Strength | 125 lb/in | Warp Direction, Substrate Property | |||
| 160 lb/in | Fill Direction, Substrate Property | ||||