- 密度 [g/cm3]: 1.28
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 76.2 microns | 3.00 mil | Interleave 1 | ||
| 76.2 microns | 3.00 mil | Interleave 2 | |||
| 152 microns | 6.00 mil | Side 1; Arlon SQA-TMS-003 | |||
| 152 microns | 6.00 mil | Side 2; Arlon SQA-TMS-003 | |||
| 203 microns | 8.00 mil | Substrate; Arlon SQA-TMS-003 | |||
| 508 microns | 20.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 83 | 83 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 7.329 MPa | 1063 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 134 % | 134 % | Silicone Property; ASTM D412 | ||
| Tear Strength | 25.2 kN/m | 144 pli | [ppiw], Die B, Silicone Property; ASTM D624 | ||
| Peel Strength | 0.526 kN/m | 3.00 pli | [ppiw], Bond Strength to 6061 aluminum (90° peel test); Arlon-SQA-TMS-011 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | ||
| Shelf Life | 6.00 Month @Temperature 7.22 °C | 6.00 Month @Temperature 45.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Red | Substrate | ||||
| Total Product Weight (oz/yd2) | 21.6 | Arlon SQA-TMS-025 | |||