| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Thickness | 76.2 microns | 3.00 mil | Polyethylene, Interleave | ||
| 457 microns | 18.0 mil | Prime Coated 162 Fiberglass, Substrate | |||
| >= 533 microns | >= 21.0 mil | Side 1 | |||
| >= 533 microns | >= 21.0 mil | Side 2 | |||
| 1400 - 1650 microns | 55.0 - 65.0 mil | Overall | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 50 - 60 | 50 - 60 | Compound Property | ||
| Tensile Strength | 6.41 - 7.38 MPa | 930 - 1070 psi | Compound Property | ||
| Elongation at Break | 470 - 530 % | 470 - 530 % | Compound Property | ||
| Tear Strength | >= 35.1 kN/m | >= 200 pli | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 30.0 min @Temperature 177 °C | 0.500 hour @Temperature 350 °F | Recommended Cure Cycle | ||
| 30.0 min @Temperature 204 °C | 0.500 hour @Temperature 400 °F | Ramp to Temp; then hold for 4 hours, Recommended Postcure Cycle | |||
| Shelf Life | 6.00 Month | 6.00 Month | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 47.5 - 52.5 | ||||
| Uncoated Fabric Break Strength | 420 lb/in | Fill Direction, Substrate Property | |||
| 700 lb/in | Warp Direction, Substrate Property | ||||