- 密度 [g/cm3]: 1.35
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Density | 1.35 g/cc | 0.0488 lb/in³ | Side 1, Silicone Property; Arlon SQA-TMS-024 | ||
1.35 g/cc | 0.0488 lb/in³ | Side 2, Silicone Property; Arlon SQA-TMS-024 | |||
Thickness | 76.2 microns | 3.00 mil | Polyethylene, Interleave | ||
457 microns | 18.0 mil | Style 162 Fiberglass, Substrate; Arlon SQA-TMS-003 | |||
533 microns | 21.0 mil | Side 1; Arlon SQA-TMS-003 | |||
533 microns | 21.0 mil | Side 2; Arlon SQA-TMS-003 | |||
1520 microns | 60.0 mil | Overall; Arlon SQA-TMS-003 | |||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Shore A | 60 | 60 | Side 1, Silicone Property; ASTM D2240 | ||
60 | 60 | Side 2, Silicone Property; ASTM D2240 | |||
Tensile Strength | 5.52 MPa | 800 psi | Side 1, Silicone Property; ASTM D412 | ||
6.21 MPa | 900 psi | Side 2, Silicone Property; ASTM D412 | |||
Elongation at Break | 225 % | 225 % | Side 1, Silicone Property; ASTM D412 | ||
225 % | 225 % | Side 2, Silicone Property; ASTM D412 | |||
Tear Strength | 15.8 kN/m | 90.0 pli | [ppiw], Side 1, Silicone Property; ASTM D624 | ||
15.8 kN/m | 90.0 pli | [ppiw], Side 2, Silicone Property; ASTM D624 | |||
Electrical Properties | Metric | English | Comments | ||
Dielectric Strength | 15.7 kV/mm | 400 kV/in | ASTM D149 | ||
Thermal Properties | Metric | English | Comments | ||
Maximum Service Temperature, Air | 232 °C | 450 °F | |||
Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
UL RTI, Electrical | 220 °C | 428 °F | E54153 | ||
UL RTI, Mechanical without Impact | 220 °C | 428 °F | E54153 | ||
Processing Properties | Metric | English | Comments | ||
Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
Shelf Life | 60.0 Month @Temperature 23.9 °C | 60.0 Month @Temperature 75.0 °F | From date of manufacture | ||
Descriptive Properties | |||||
Color | Red | ||||
Total Product Weight (oz/yd2) | 60 | Arlon SQA-TMS-025 |