| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Thickness | 76.2 microns | 3.00 mil | Interleave | ||
| 88.9 microns | 3.50 mil | Side 1; Arlon SQA-TMS-003 | |||
| 178 microns | 7.00 mil | Side 2; Arlon SQA-TMS-003 | |||
| 457 microns | 18.0 mil | Substrate; Arlon SQA-TMS-003 | |||
| 724 microns | 28.5 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 60 | 60 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 6.76 MPa | 980 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 220 % | 220 % | Silicone Property; ASTM D412 | ||
| Tear Strength | 17.0 kN/m | 97.0 pli | {ppiw], Die B, Silicone Property; ASTM D624 | ||
| Peel Strength | 2.54 kN/m | 14.5 pli | (S1 to S1) Bond Strength; Arlon SQA -TMS-011 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 16.3 kV/mm | 414 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 121 °C | 0.250 hour @Pressure 50.0 psi, Temperature 250 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 29.6 | Arlon SQA-TMS-025 | |||