- 密度 [g/cm3]: 1.44
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 50.8 microns | 2.00 mil | Substrate; Arlon SQA-TMS-003 | ||
| 63.5 microns | 2.50 mil | Side 1; Arlon SQA-TMS-003 | |||
| 63.5 microns | 2.50 mil | Side 2; Arlon SQA-TMS-003 | |||
| 63.5 microns | 2.50 mil | Interleave 1 | |||
| 63.5 microns | 2.50 mil | Interleave 2 | |||
| 178 microns | 7.00 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 73 | 73 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 7.58 MPa | 1100 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 87 % | 87 % | Silicone Property; ASTM D412 | ||
| Tear Strength | 7.89 kN/m | 45.0 pli | Die B, Silicone Property; ASTM D624 | ||
| Peel Strength | 0.193 kN/m | 1.10 pli | Bond Strength; Arlon SQA -TMS-011 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 121 °C | 0.250 hour @Pressure 50.0 psi, Temperature 250 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Slate Gray | ||||
| White | Substrate | ||||
| Fuel Resistance | 0.118 | Fuel CM85 resistance, ASTM D471 | |||
| 0.139 | Fuel A resistance, ASTM D471 | ||||
| 0.269 | Fuel C resistance, ASTM D471 | ||||
| Total Product Weight (oz/yd2) | 8.6 | Arlon SQA-TMS-025 | |||