- 密度 [g/cm3]: 2.4
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 2.40 g/cc | 0.0867 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 25.4 microns | 1.00 mil | Liner | ||
| 76.2 microns | 3.00 mil | Carrier | |||
| 203 microns | 8.00 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 50 | 50 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 2.76 MPa | 400 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 245 % | 245 % | Silicone Property; ASTM D412 | ||
| Modulus of Elasticity | 0.00345 GPa @Strain <=1.00 % | 0.500 ksi @Strain <=1.00 % | Silicone Property; Arlon SQA-TMS-008 | ||
| Poissons Ratio | 0.50 | 0.50 | Approximately, Silicone Property | ||
| Shear Modulus | 0.207 GPa @Strain <=100 % | 30.0 ksi @Strain <=100 % | ASTM D1002 | ||
| Shear Strength | 2.00 MPa | 290 psi | Lap Shear Strength; ASTM D1002 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 5.4 @Frequency 1.00e+6 Hz | 5.4 @Frequency 1.00e+6 Hz | Dk, Silicone Property; IPC TM 650-2.5.5.3 | ||
| Dielectric Strength | 30.9 kV/mm | 785 kV/in | ASTM D149 | ||
| Dissipation Factor | 0.0050 @Frequency 1.00e+6 Hz | 0.0050 @Frequency 1.00e+6 Hz | Df, Silicone Property; IPC TM 650-2.5.5.3 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 134 µm/m-°C | 74.4 µin/in-°F | Silicone Property; ASTM E 831 | ||
| Specific Heat Capacity | 0.900 J/g-°C @Temperature 100 °C | 0.215 BTU/lb-°F @Temperature 212 °F | Silicone Property; ASTM E 1952 | ||
| Thermal Conductivity | 1.64 W/m-K | 11.4 BTU-in/hr-ft²-°F | Product Property; ASTM E 1530 | ||
| 1.00 W/m-K @Temperature 100 °C | 6.94 BTU-in/hr-ft²-°F @Temperature 212 °F | Silicone Property; ASTM E 1530 | |||
| Maximum Service Temperature, Air | 204.0 °C | 399.2 °F | |||
| Minimum Service Temperature, Air | -100 °C | -148 °F | |||
| Glass Transition Temp, Tg | -118 °C | -180 °F | Silicone Property; ASTM D3418 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Pressure 0.101 - 0.345 MPa, Temperature 121.0 °C | 0.250 hour @Pressure 14.6 - 50.0 psi, Temperature 249.8 °F | Recommended Cure Cycle | ||
| Shelf Life | 6.00 Month @Temperature 4.00 - 10.0 °C | 6.00 Month @Temperature 39.2 - 50.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Gray | ||||
| Plasticity | 2 mm | Arlon SQA-TMS-005 | |||
| Total Product Weight (g/m2) | 487 | Arlon SQA-TMS-025 | |||