- 密度 [g/cm3]: 1.6
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 25.4 microns | 1.00 mil | Liner | ||
| 76.2 microns | 3.00 mil | Carrier | |||
| 203 microns | 8.00 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 83 | 83 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 4.48 MPa | 650 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 25 % | 25 % | Silicone Property; ASTM D412 | ||
| Shear Modulus | 0.0000689 GPa | 0.0100 ksi | ASTM D1002 | ||
| Shear Strength | 2.62 MPa | 380 psi | Lap Shear Strength; ASTM D1002 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 39.4 kV/mm | 1000 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 0.800 W/m-K | 5.55 BTU-in/hr-ft²-°F | Silicone Property; ASTM E 1530 | ||
| 1.35 W/m-K | 9.37 BTU-in/hr-ft²-°F | Product Property; ASTM E 1530 | |||
| Maximum Service Temperature, Air | 204 °C | 400 °F | |||
| Minimum Service Temperature, Air | -73.3 °C | -100 °F | |||
| Glass Transition Temp, Tg | -116 °C | -177 °F | Silicone Property; ASTM D1356 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Temperature 141 °C | 0.250 hour @Temperature 285 °F | Recommended Cure Cycle | ||
| Shelf Life | 6.00 Month @Temperature 4.44 - 10.0 °C | 6.00 Month @Temperature 40.0 - 50.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | White | ||||
| Total Product Weight (g/m2) | 325 | Arlon SQA-TMS-025 | |||