Arlon P29609R025 0.025" (0.635 mm) Silicone Rubber with Fiberglass Substrate

Arlon P29609R025 0.025" (0.635 mm) Silicone Rubber with Fiberglass Substrate 物性表: Arlon P29609R025 0.025" (0.635 mm) Silicone Rubber with Fiberglass Substrate物性表及特性介绍,Arlon P29609R025 0.025" (0.635 mm) Silicone Rubber with Fiberglass Substrate注塑参数详情,如需Arlon P29609R025 0.025" (0.635 mm) Silicone Rubber with Fiberglass Substrate下载, 可到相关下载区下载
 
Physical PropertiesMetricEnglishComments
Thickness 38.1 microns1.50 milPolyethylene, Interleave
 50.8 microns2.00 milSide 1, Side 1, Fully Cured
 203 microns8.00 milPrime Coated 7628 Fiberglass, Substrate
 381 microns15.0 milSide 1, Side 2, Uncured
 610 - 660 microns24.0 - 26.0 milOverall
 
Mechanical PropertiesMetricEnglishComments
Hardness, Shore A 55 - 6555 - 65Compound Property
Tensile Strength >= 6.21 MPa>= 900 psiCompound Property
Elongation at Break >= 200 %>= 200 %Compound Property
Peel Strength >= 0.877 kN/m>= 5.00 pliBond Strength
 
Electrical PropertiesMetricEnglishComments
Dielectric Strength >= 15.7 kV/mm>= 400 kV/in
 
Thermal PropertiesMetricEnglishComments
Maximum Service Temperature, Air 260 °C500 °F
Minimum Service Temperature, Air -56.7 °C-70.0 °F
Flammability Test <= 3.0<= 3.0[in], Char Length; FTMS 191A; Method 5903
 <= 15<= 15[sec], Flame & Glow Time; FTMS 191A; Method 5903
 
Processing PropertiesMetricEnglishComments
Cure Time  15.0 min
@Temperature 177 °C
0.250 hour
@Temperature 350 °F
Recommended Cure Cycle
 120 min
@Temperature 204 °C
2.00 hour
@Temperature 400 °F
Recommended Postcure Cycle
Shelf Life 6.00 Month
@Temperature 23.9 °C
6.00 Month
@Temperature 75.0 °F
From date of manufacture
 
Descriptive Properties
ColorRed
Total Product Weight (oz/yd2)24.4 - 28.4
Uncoated Fabric Break Strength200 lb/inFill Direction, Substrate Property
 250 lb/inWarp Direction, Substrate Property

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-34229.html

免责声明: 本文 Arlon P29609R025 0.025" (0.635 mm) Silicone Rubber with Fiberglass Substrate 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4