- 密度 [g/cm3]: 3.7
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 3.70 g/cc | 0.134 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 25.4 microns | 1.00 mil | Liner | ||
| 76.2 microns | 3.00 mil | Carrier | |||
| 381 microns | 15.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 84 | 84 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 3.34 MPa | 485 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 60 % | 60 % | Silicone Property; ASTM D412 | ||
| Modulus of Elasticity | 0.01957 GPa | 2.838 ksi | ASTM E 831 | ||
| Poissons Ratio | 0.50 | 0.50 | Approximately, Silicone Property | ||
| Shear Modulus | 0.000379 GPa | 0.0550 ksi | ASTM D 1002 | ||
| Shear Strength | 3.65 MPa | 530 psi | Lap Shear Strength; ASTM D1002 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 500 ohm-cm | 500 ohm-cm | Silicone Property; ASTM D991 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 93.0 µm/m-°C | 51.7 µin/in-°F | Silicone Property; ASTM E 831 | ||
| Specific Heat Capacity | 0.400 J/g-°C | 0.0956 BTU/lb-°F | E 1461-01 | ||
| Thermal Conductivity | 0.750 W/m-K | 5.20 BTU-in/hr-ft²-°F | Silicone Property; ASTM E 1530 | ||
| Maximum Service Temperature, Air | 204 °C | 400 °F | |||
| Minimum Service Temperature, Air | -73.3 °C | -100 °F | |||
| Glass Transition Temp, Tg | <= -100 °C | <= -148 °F | Silicone Property; ASTM D3418 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Temperature 141 °C | 0.250 hour @Temperature 285 °F | Recommended Cure Cycle | ||
| Shelf Life | 6.00 Month @Temperature -15.0 - -9.44 °C | 6.00 Month @Temperature 5.00 - 15.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Naturally Gray | ||||
| Total Product Weight (g/m2) | 1410 | Arlon SQA-TMS-025 | |||