- 密度 [g/cm3]: 1.22
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 127 microns | 5.00 mil | Substrate; Arlon SQA-TMS-003 | ||
| 508 microns | 20.0 mil | Silicone; Arlon SQA-TMS-003 | |||
| 635 microns | 25.0 mil | Overall Thickness; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 45 | 45 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 6.38 MPa | 925 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 550 % | 550 % | Silicone Property; ASTM D412 | ||
| Peel Strength | 3.86 kN/m | 22.0 pli | Bond Strength; Arlon SQA-TMS-011 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 29.5 kV/mm | 750 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Inert | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Post Cure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 149 °C | 0.250 hour @Pressure 50.0 psi, Temperature 300 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | |||
| Descriptive Properties | |||||
| Color | Gray | Silicone | |||
| White | Substrate | ||||
| Total Product Weight (oz/yd2) | 23.8 | Arlon SQA-TMS-025 | |||