- 密度 [g/cm3]: 1.22
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 76.2 microns | 3.00 mil | Side 1; Arlon SQA-TMS-003 | ||
| 102 microns | 4.00 mil | Substrate; Arlon SQA-TMS-003 | |||
| 127 microns | 5.00 mil | Side 2; Arlon SQA-TMS-003 | |||
| 305 microns | 12.0 mil | Overall Thickness; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 36 | 36 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 6.21 MPa | 900 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 550 % | 550 % | Silicone Property; ASTM D412 | ||
| Tear Strength | 14.0 kN/m | 80.0 pli | Silicone Property; ASTM D624 | ||
| Peel Strength | 2.56 kN/m | 14.6 pli | Bond Strength (S1 to S2); Arlon SQA-TMS-011 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 33.3 kV/mm | 845 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Inert | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability Test | 1.1 | 1.1 | Inches; Char Length; FAR 25.853 App F, Pt. 1, S. A1ii | ||
| 6.3 | 6.3 | Seconds; Flame and Glow Time; FAR 25.853 App F, Pt. 1, S. A1ii | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Post Cure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | |||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 10.7 | Arlon SQA-TMS-025 | |||