- 密度 [g/cm3]: 1.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 38.1 microns | 1.50 mil | Interleave | ||
| 50.8 microns | 2.00 mil | Side 1; Arlon SQA-TMS-003 | |||
| 50.8 microns | 2.00 mil | Substrate; Arlon SQA-TMS-003 | |||
| 140 microns | 5.50 mil | Overall thickness; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 60 | 60 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 5.72 MPa | 830 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 150 % | 150 % | Silicone Property; ASTM D412 | ||
| Tear Strength | 9.64 kN/m | 55.0 pli | Die B; Silicone Property; ASTM D624 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Inert | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability Test | 1.0 | 1.0 | Flame and Glow (seconds); FAR 25.853 App.F, P.1, S.Aii | ||
| 2.0 | 2.0 | Char Length (inches); FAR 25.853 App.F, P.1, S.Aii | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Post Cure Cycle | ||
| Shelf Life | 60.0 Month @Temperature 23.9 °C | 60.0 Month @Temperature 75.0 °F | |||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 6 | Arlon SQA-TMS-025 | |||