- 密度 [g/cm3]: 1.81
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.81 g/cc | 0.0654 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 127 microns | 5.00 mil | Carrier; Arlon SQA-TMS-003 | ||
| 1520 microns | 60.0 mil | Side 1; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 65 | 65 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 3.85 MPa | 558 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 82 % | 82 % | Silicone Property; ASTM D412 | ||
| Tear Strength | 4.91 kN/m | 28.0 pli | Die B; Silicone Property; ASTM D624 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Inert | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Post Cure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 121 °C | 0.250 hour @Pressure 50.0 psi, Temperature 250 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | |||
| Descriptive Properties | |||||
| Color | Light Green | Product | |||
| Translucent | Carrier | ||||
| Fuel A Resistance (% vol. swell) | 6 | ASTM D471 | |||
| Fuel C Resistance (% vol. swell) | 18.7 | ASTM D471 | |||
| Fuel CM85 Resistance (% vol. swell) | 11.9 | ASTM D471 | |||
| Total Product Weight (oz/yd2) | 81.4 | Arlon SQA-TMS-025 | |||