- 密度 [g/cm3]: 1.24
- 拉伸强度 [MPa]: 9.2
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D3165 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 89 | 89 | ASTM D2240 | ||
| 95.23 @Treatment Temp. 125 °C, Time 252000 sec | 95.23 @Treatment Temp. 257 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Tensile Strength, Yield | 9.20 MPa | 1330 psi | ASTM D412 | ||
| 7.3968 MPa @Treatment Temp. 125 °C, Time 252000 sec | 1072.8 psi @Treatment Temp. 257 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Elongation at Break | 194.8 % | 194.8 % | ASTM D412 | ||
| 78.894 % @Treatment Temp. 125 °C, Time 252000 sec | 78.894 % @Treatment Temp. 257 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Compressive Modulus | 0.00135 GPa @Strain 5.00 % | 0.196 ksi @Strain 5.00 % | |||
| 0.00236 GPa @Strain 10.0 % | 0.342 ksi @Strain 10.0 % | ||||
| 0.00516 GPa @Strain 20.0 % | 0.748 ksi @Strain 20.0 % | ||||
| 0.00589 GPa @Strain 25.0 % | 0.854 ksi @Strain 25.0 % | ||||
| Compression Set | 6.6 % @Temperature 100 °C, Time 252000 sec | 6.6 % @Temperature 212 °F, Time 70.0 hour | ASTM D395 | ||
| Descriptive Properties | |||||
| Color | Black | ||||